Researchers optimize the assembly of micro-/meso-/macroporous carbon for Li-S batteries



Li-S batteries are considered as promising alternatives for Li-ion batteries in the new generation of energy storage, due to high specific capacity (1675 mAh/g) and energy density (2600 mWh/g) of sulfur. But the poor conductivity of sulfur and severe shuttle effect of reaction intermediates destory the stability of this system. A variety of porous carbon materials have been applied as sulfur host to improve the performances of Li-S batteries for high conductivity, specific surface area and absorption effect. However, what kind of porous carbon would be the optimal choice to accommodate active material? And Which characteristic of carbon pores should be emphasized?

A team of researchers from the School of Materials Science and Engineering and School of Electronic Science and Applied Physics at Hefei University of Technology demonstrated that pore size distribution substantially influences the performances of cathode rather than specific surface area and total pore volume. Furthermore, an optimized assembly of micro/meso/macroporous carbon enables cathode present greatly improved electrochemical performances, in which micropore-volume-ratio to the total pore volume dominates cycling stability of batteries, meso/macropore-volume-ratio influences spaces for sulfur loading and channels to ion transfer. This research provides a direction of fabricating porous materials for energy storage.The report appears in the latest issue of the journal NANO.

Based on the traditional S/C cathode, the effects of surface area, total pore volume and pore size distribution of carbon pores on performances of Li-S batteries are compared. In addition, on the premise of identically high sulfur content, the relation of the micro/meso/macropore volume ratio with the capacity, voltage plateau, rate capability, and cycle stability of Li-S battery are investigated. Among the samples, the porous carbon possesses the largest micropore volume ratio of 47.54% while a medium specific surface area of 1217 m2/g and inferior total pore volume of 0.54 cm3/g presents the highest initial discharge specific capacity of 1327 mAh/g and retention of 630 mAh/g over 100 cycles at 0.2C rate along with the best rate capability. The conclusions in this study can be directly applied in material fabrication for other systems of energy storage and even as criterions for further modification of Li-S batteries based on carbon material.

This research was supported by the "Strategic Priority Research Program" of the Chinese Academy of Science (NO. XDA03040000) and the Fundamental Research Funds for the Central Universities (NO. 103-4115100010) of China.

Additional co-authors of the NANO paper are Min Zuo, Jing Zhang, Yiqin Huang, Peiwen Bai, Jiaqi Xu, Kuan Zhou.

Hefei University of Technology

#Energy #Batteries

 

STAY CURRENT WITH THE NWA NEWSLETTER DELIVERED TO YOUR INBOX.

FOUNDING MEMBERS

Manipulating non-magnetic atoms in a chromium halide enables tuning of magnetic properties

Tailored light inspired by nature

Novel approach improves graphene-based supercapacitors

Metal-Breathing Bacteria Could Transform Electronics, Biosensors, and More

Scientists discover new class of semiconducting entropy-stabilized materials

Mapping crystal shapes could fast-track 2D materials

Origami metamaterials show reversible auxeticity combined with deformation recoverability