Nano-Clear Matte Finish Protective Overcoat

By Nanovere Technologies, LLC

Designed to Protect the Warfighter. Extends the Service Life of Military Assets. Reduce Paint Cycle by 5X. As Documented in Production Case Studies. 50X Reduced Chemical Absorption. Chemical & Biological Resistance (sarin, anthrax...). Extreme Abrasion Resistance - Only 1.1 mg loss after 1000 cycles, 1 kg. Extreme Corrosion Resistance - No Rust After 6000 Hour Salt Spray Testing. Extreme Chemical Resistance - Outperformed all CARC Competitors: DEVCOM. Weatherproof Technology. Matte Clear Overcoating. Return to Service in 24 hours. 99% Retention after 4000 Hours - Xenon WOM. Nano-Clear Overcoat is designed to be applied directly "over" pigmented CARC paints, as a clear matte finish overcoating. The Nano-Clear Overcoat dramatically extends the service life of military painted assets by significantly improving decontamination, corrosion resistance, abrasion, scratch, chemical and weathering resistance. Nano-Clear Overcoat significantly reduces decontamination time while preventing biological agents from penetrating into military paint and allows for easier removal during the decontamination process. Nano-Clear® Overcoat is manufactured using proprietary 3D nanostructured polymers - producing extreme crosslink density. Nano-Clear Overcoat is a two-component clear matte finish over-coating providing extreme corrosion resistance, abrasion, chemical & UV resistance and reduced surface maintenance. Nano-Clear Overcoat penetrates deep into the pores of CARC paints to dramatically improve corrosion resistance, surface hardness, chemical and long-term UV resistance with 50% reduced surface tension. Nano-Clear Overcoat produces an exceptionally high crosslink dense polymer network designed to withstand harsh environments. Nano-Clear Overcoat is the world's first clear matte finish designed to be applied directly OVER conventional CARC paints. Stonebridge Coatings Laboratory has validated Nano-Clear Overcoat to have the highest scratch resistance and chemical resistance over other leading CARC paints when used alone. What Makes Nano-Clear so Unique? Nano-Engineering Creates Exceptional Crosslink Density: Coatings contain "building blocks" with functional groups. The chemical reaction of these groups during curing forms a network. In most traditional polymers, the network is a linear chain of molecules with low crosslink density. Conversely, we "nano-structured" our clearcoat to have a 3D molecular architecture. The 3D polymer network has an exponentially higher number of crosslinked sites. The result is a tightly knit mesh with unprecedented DMA density. High crosslink density provides highly functional surface properties, including unmatched corrosion resistance, scratch resistance, chemical resistance and UV durability. It also means low surface energy, repelling water (hydrophobic) and aiding in the release of ice, dirt, brake dust, and even concrete dust. Specifications: Crosslink Density 2.17 (X10 3 mol/m 3); VOC 1.05 lb/gal (150 g/l); Recommended Dry Film Thickness 2 - 3 mils; Coverage 330 sq ft/gal (at 2 mil); Gloss 20° / 60° 0.60 / 1; Abrasion Resistance (CS-17, 1 kg, 1000 cycles) 8.4 mg loss; Pencil Hardness, Scratch 7H; Scratch Hardness 2500 gm; Pencil Hardness, Gouge 7H; Pendulum Hardness (Persoz) > 250 oscillations; Impact Resistance 18°C Direct 50 Pass / 60 Fail in/lbs; Impact Resistance 18°C Reverse 10 Pass / 20 Fail in/lbs; Impact Strength 1 kg - 160 cm; Chip Resistance 23°C (2 mils) 145 kg-cm; Chip Resistance -29°C (2 mils) 7A; Falling Sand Abrasion 100 liters 7B Pass; Mar Resistance 5.0 kg; Xenon WOM Resistance 4000 hrs 100% Gloss Retention; QUV 313, >1500 hrs 99% Gloss Retention; Water Immersion Test 240 hrs @ 50°C 100% Gloss Retention; Salt Spray, 4000 hrs Pass; Humidity, 100% RH, 100°F, 240 hrs Excellent; CASS 240 hrs @ 50°C No loss of adhesion. No change; Thermal Shock (100°F 3 hrs, Freeze 3 hrs, Steam Blast 30 sec) Pass; 10% Sulfuric Acid No loss of adhesion. No Change; 10% Hydrochloric Acid No effect; 10% Sodium Hydroxide No effect; 10% Ammonium Hydroxide No effect; Isopropyl Alcohol No effect; Xylene No effect; Skydrol ® 500 Fluid No effect; MEK Resistance 1500 double rubs; Adhesion, Direct to Metal 3 Mpa Rating 10; Adhesion, Cross Cut Passed (Very Good); Flexibility, 1mm Mandrel 3 mm Passed (Excellent); Flexibility, Cylindrical Mandrel Class 1 (Excellent); Flammability: Fire Retardant & Flame Spread It was possible to flake off ice bits and melting was faster; De-Icing Aid Oil & Dirt Release; Self-Cleaning Properties Hydrophobic, Brake-Dust Release; Pot Life 20% to 80%; Viscosity 20 cps; Spray Applicators HVLP, Conventional or Airless; Wipe-On Application ShurLine ® Deck Pad; Application Temp 40°F to 90°F; Operating (Service) Temp -40°F to 250°F; DMA (Dynamic Mechanical Analysis) Relative Humidity; Dry Time: Dust Free @ 68-72°F 30 minutes; Dry-To-Handle @ 68-72°F 4 hours. Recommended Uses: Newly Painted or Existing CARC Paints. Chemistry: Nano-Structured Polyurethane Hybrid.