Developing a lightweight material that is both strong and highly ductile has been regarded as a long-desired goal in the field of structural materials, but these properties are generally mutually exclusive. Researchers at City University of Hong Kong (CityU) recently discovered a low-cost, direct method to turn commonly used 3D printable polymers into lightweight, ultra-tough, biocompatible hybrid carbon microlattices, which can be in any shape or size, and are 100 times stronger than the original polymers. The research team believes that this innovative approach can be used to create sophisticated 3D parts with tailored mechanical properties for a wide range of applications, including coronary stents and bio-implants.
Metamaterials are materials engineered to have properties that are not found in naturally occurring materials. 3D architected metamaterials, such as microlattices, combine the benefits of lightweight structural design principles with the intrinsic properties of their constituent materials. Making these microlattices often requires advanced fabrication technologies, such as additive manufacturing (commonly referred to as 3D printing), but the range of materials available for 3D printing is still fairly limited.
“3D printing is becoming a ubiquitous technology for producing geometrically complex components with unique and tuneable properties. Strong and tough architected components usually require metals or alloys to be 3D printed, but they are not easily accessible owing to the high cost and low resolution of commercial metal 3D printers and raw materials. Polymers are more accessible but typically lack mechanical strength or toughness. We found a way to convert these weaker and brittle 3D-printed photopolymers into ultra-tough 3D architectures comparable to metals and alloys just by heating them under the right conditions, which is surprising,” said Professor Lu Yang in the Department of Mechanical Engineering (MNE) and Department of Materials Science and Engineering (MSE) at CityU, who led the research.
A new method to increase strength without compromising ductility
So far, the most effective approach for increasing the strength of these 3D printable polymer lattices is pyrolysis, a thermal treatment that transforms the entire polymers into ultra-strong carbon. However, this process deprives the original polymer lattice of almost all its deformability and produces an extremely brittle material, like glass. Other methods to increase the strength of the polymers also typically result in compromising their ductility.
The team led by Professor Lu found a “magic-like” condition in the pyrolysis of the 3D-printed photopolymer microlattices, which resulted in a 100-fold increase in strength and doubled the ductility of the original material. Their findings were published in the scientific journal Matter under the title “Lightweight, Ultra-tough 3D Architected Hybrid Carbon Microlattices”.
They discovered that by carefully controlling the heating rate, temperature, duration and gas environment, it is possible to simultaneously enhance the stiffness, strength and ductility of a 3D-printed polymer microlattice drastically in a single step.
Through various characterization techniques, the team found that simultaneous improvement in strength and ductility is possible only when the polymeric chains are “partially carbonized” by slow heating, where incomplete conversion of the polymer chains to pyrolytic carbon occurs, producing a hybrid material in which both loosely cross-linked polymer chains and carbon fragments synergistically coexist. The carbon fragments serve as reinforcing agents that strengthen the material, while the polymer chains restrict the fracture of the composite.
The contrasting mechanical behaviours of partially carbonized structures compared to the original polymer structure. The scale bars represent 2mm. @ Surjadi, James et al., /doi.org/10.1016/j.matt.2022.08.010
The ratio of polymer to carbon fragments is also crucial to obtaining optimal strength and ductility. If there are too many carbon fragments, the material becomes brittle, and if there are too few, the material lacks strength. During the experiments, the team successfully created an optimally carbonized polymer lattice that was over 100 times stronger and over two times more ductile than the original polymer lattice.
Benefits beyond mechanical property enhancement
The research team also found that these “hybrid carbon” microlattices showed improved biocompatibility compared to the original polymer. Through cytotoxicity and cell behaviour monitoring experiments, they proved that the cells cultured on the hybrid carbon microlattices were more viable than cells seeded on the polymer microlattices. The enhanced biocompatibility of the hybrid-carbon lattices implies that the benefits of partial carbonization may go beyond enhancement in mechanical performance and potentially improve other functionalities as well.
“Our work provides a low-cost, simple and scalable route for making lightweight, strong and ductile mechanical metamaterials with virtually any geometry,” said Professor Lu. He envisions that the newly invented approach can be applied to other types of functional polymers, and that the geometrical flexibility of these architected hybrid-carbon metamaterials will allow their mechanical properties to be tailored for a wide range of applications, such as biomedical implants, mechanically robust scaffolds for micro-robots, energy harvesting and storage devices.
Reference
Lightweight, ultra-tough, 3D-architected hybrid carbon microlattices
James Utama Surjadi, Yongsen Zhou, Siping Huang, Liqiang Wang, Maoyuan Li, Sufeng Fan, Xiaocui Li, Jingzhuo Zhou, Raymond H.W. Lam, Zuankai Wang, Yang Lu
Researchers at the University of Córdoba have used vitamin B12, or cobalamin, as a catalyst in a zinc-air battery for the first time, anchoring the biomolecule to single-walled carbon nanotubes to keep it stable in an aqueous electrolyte. The cobalt at its core drives oxygen reduction on discharge and oxygen production on recharge, enabling up to 250 cycles.
A one-step liquid coating that converts into a 12-micrometer hybrid film on lithium metal could bring solid-state batteries closer to practical use. The polysiloxane and indium chloride layer forms lithium fluoride and lithium-indium alloy nanoparticles in situ, suppressing dendrite growth. Protected anodes reached 3.5 mA cm-2 critical current density and retained 82.3% capacity after 300 cycles in full cells with a sulfide electrolyte and NCM cathode, versus 43.0% for bare lithium.
Researchers at Jilin University and the Changchun Institute of Applied Chemistry have shown that hydroxyl functional groups on self-supporting carbon nanotube cathodes stabilize aqueous zinc-iodine batteries. Density functional theory guided the choice of surface groups, and the hydroxyl-modified cathode confined iodine species within its porous nanotube channels. It retained 89.34% of capacity after more than 10,000 cycles and suppressed the iodine shuttle effect.
This week in nanotech
$13.6M raised
3 funding rounds · 20 deals tracked
New products
DLS-1 Mass Spectrometer for Fusion Gas AnalysisHiden Analytical Featured
Orion Sputtering Deposition SystemsAJA International Featured
GiiiGiiMarket insights
Last 30 days: Quantum Technologies was the busiest vertical: 61 of 192 events (32%).
Money raised per month